Surface Property Evolution of Pigmented Chinese Lacquer Coatings During Mercury Lamp-Induced Photoaging
Year: 2025
Type: article
Abstract: This study examines the pigment-dependent photoaging behavior of laboratory-prepared mock-up Chinese lacquer coatings colored with cinnabar, orpiment, and lapis lazuli under high-pressure mercury-lamp irradiation. Colorimetric results showed rapid changes within the first three days, with maximum ΔE values of 14.05 (red), 16.74 (yellow), and 17.97 (blue) after 30 days. Cinnabar-based films exhibited the highest color stability, whereas orpiment and lapis-lazuli coatings underwent pronounced hue shifts and chroma increases. Gloss loss and surface roughness evolution displayed a strong negative correlation: orpiment coatings experienced the most severe degradation, with gloss decreasing by over 60% and surface roughness increasing by approximately 70%, while cinnabar coatings showed the least decline (≈55% gloss loss; ≈27% roughness increase). SEM analysis further revealed extensive cracking and particle fragmentation in orpiment films, moderate surface disruption in lapis-lazuli films, and minimal microstructural damage in cinnabar films. Non-invasive reflection-mode FTIR spectroscopy confirmed these trends, showing minimal chemical change in cinnabar coatings but significant carbonyl growth, C–O–C band broadening, and aliphatic chain cleavage in orpiment and lapis-lazuli coatings. These results highlight the critical role of pigment chemistry in modulating UV-induced degradation pathways. Integrating optical, morphological, and chemical evidence, this study establishes a clear pigment-dependent degradation mechanism and provides valuable guidance for evaluating the long-term stability of lacquered cultural heritage and optimizing modern lacquer formulations.
Source: Coatings
Authors: Yunxi Nie, Yushu Chen, Xinyou Liu
Institution: Nanjing Forestry University
Language: English
Subfield: Archeology
Field: Arts and Humanities
Domain: Social Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W7117453891