Unveiling the synergistic mechanism of magnesium hydroxide and silica in modulating polyethersulfone membrane structure and function

Year: 2026

Type: article

Abstract: In this study, an environmentally benign dual-additive modification strategy was investigated by incorporating magnesium hydroxide and silica into PES membranes to simultaneously tailor surface chemistry and pore morphology during non-solvent-induced phase separation. Membranes were fabricated using a fixed Mg(OH) 2 content with varying silica concentrations and characterized by FESEM, ATR-FTIR, gravimetric porosity analysis, water contact angle measurements, and filtration performance testing, including pure-water flux, humic acid rejection, and flux recovery ratio. All modified membranes retained the asymmetric structure of pristine PES but developed thinner selective layers and more elongated finger-like macrovoids as silica content increased up to the optimum composition (M-MS2.5). At this condition, porosity increased to 67.73%, the O–H absorption band became more pronounced, and the water contact angle decreased from ∼80° to 53.4° (≈33% reduction), indicating enhanced interfacial hydrophilicity. These structural and chemical enhancements led to improved transport and fouling behavior, with water flux approaching ∼80 L·m -2 ·h -1 and the flux recovery ratio increasing to 90.91%. Although humic acid rejection decreased from 79.8% (pristine) to 69.19% at the optimum silica loading (2.5%), it remained within a reasonable ultrafiltration performance range. At higher silica concentrations, however, particle agglomeration and localized structural densification were observed, resulting in increased contact angle, reduced flux, and partial recovery of rejection, indicating a limited compositional window for effective synergy between silica and Mg(OH) 2 . Overall, the intermediate silica loading (2.5 wt%) provided the most favorable balance between permeability, antifouling stability, and rejection, suggesting strong potential for application in high-throughput treatment of NOM-rich waters. • Synergistic Mg(OH) 2 –silica dual additives effectively enhance PES membrane hydrophilicity • Dual-additive incorporation tailors pore architecture and increases membrane porosity • Optimal silica loading achieves high water flux with controlled humic acid rejection • Antifouling performance is significantly improved via hydration-layer formation • Mg(OH) 2 –silica modified PES membranes show strong potential for sustainable NOM-rich water treatment

Source: Case Studies in Chemical and Environmental Engineering

DOI: 10.1016/j.cscee.2026.101328