Investigation of the Hydration and Solidification Effect of Peanut Ash Cement-Based Stabilizer in Soft Clay Treatment

Year: 2026

Type: article

Abstract: To promote the sustainable utilization of agricultural solid waste, this study proposes a novel approach for reinforcing soft clay using a peanut ash (PA)-cement composite stabilizer. The unconfined compressive strength (UCS) of pure cement and PA-cement composite systems was tested at curing ages of 3, 7, and 28 days, while the durability of the stabilized clay was evaluated through dry-wet cycling. Given that PA is rich in pozzolanic components, its addition may influence the hydration process of cement. Therefore, hydration heat analysis was conducted to examine the early hydration behavior, and XRD and TG analyses were employed to identify the composition and quantity of hydration products. SEM observations were further used to characterize the microstructural evolution of the stabilized matrix. By integrating mechanical and microstructural analyses, the solidification mechanism of the PA-cement stabilizer was elucidated. Mechanical test results indicate that the reinforcing effect increases with the stabilizer dosage. Pure cement exhibited superior strength at 3 days; however, after 7 days, specimens incorporating 5% PA showed higher strength than those stabilized solely with cement. At 28 days, the UCS of the 15% cement + 5% PA specimen reached 3.12 MPa, 11.03% higher than that of the 20% cement specimen and comparable to the 25% cement specimen (3.15 MPa). After five dry-wet cycles, the strength reduction of the 15% cement + 5% PA specimen was 22.76%, compared to 31.31% for the 20% cement specimen, indicating improved durability. Microscopic analyses reveal that PA reduces hydration heat and does not participate in early hydration, leading to lower early strength. However, its pozzolanic reactivity contributes to secondary hydration at later stages, promoting the formation of additional C-S-H gel and ettringite. These hydration products fill the inter-lamellar pores of the clay and increase matrix density. Conversely, excessive PA content (≥10%) exerts a dilution effect, reducing the amount of hydration products and weakening the mechanical performance. Overall, the use of an appropriate PA dosage in combination with cement enhances both strength and durability while reducing cement consumption, providing an effective pathway for the high-value utilization of agricultural solid waste resources.

Source: Materials

DOI: 10.3390/ma19020318

Authors: Yongqin Qiu, Qichang Fan, Kun Zhang

Institutions: Sun Yat-sen University, South China University of Technology

Language: English

Topic: Geotechnical Engineering and Soil Stabilization

Subfield: Civil and Structural Engineering

Field: Engineering

Domain: Physical Sciences

SDGs: Responsible consumption and production, Industry, innovation and infrastructure

Open Access status: gold

Estimated APC paid: $3,137