Enhancement of ductility and resistance to hydrogen embrittlement in laser powder-bed fusion Ti−6Al−4V alloy by reversible transformation
Year: 2025
Type: article
Abstract: To simultaneously enhance the strength−plasticity synergy and resistance to hydrogen embrittlement (HE), the post-annealing treatment was conducted in a laser powder-bed fusion Ti−6Al−4V alloy to introduce reversible transformation. The microstructure, mechanical properties, and HE behavior of the alloy were analyzed by electron back-scattered diffraction, transmission electron microscopy, slow-strain-rate tensile test, hydrogen permeation and thermal desorption spectroscopy. The as-printed sample exhibited high strength but limited elongation and high HE sensitivity. When annealed at 550 °C, the elongation was improved but the hydrogen diffusion rate also increased, thus promoting the formation of brittle hydride. When annealed at 750 °C, the reversible transformation α’ → β → α’ occurred and an α’ / β / α’ sandwich structure formed, thereby enhancing HE resistance (reducing the total elongation loss to 12%) while maintaining high strength (~1116 MPa). The introduction of nanoscale β -phase and soft-oriented α’ grain significantly inhibited hydride formation and hydrogen-induced crack propagation.
Authors: Huan-qi MA, Yu LI, Wei LI, Chun XU
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W7125520201