Quantifying Thermoset Cure State During Fabrication of a Laminated Composite Using Ultrasonic Waveform Analysis

Year: 2026

Type: article

Abstract: Fiber-reinforced laminates composed of a thermoset matrix have seen widespread use in industries such as the aerospace, wind power, and automotive industries, due to their strength-to-weight ratios and ease of formability. For optimal performance, the instantaneous cure state must be sufficient such that the component will not deform during or after molding, a state that can vary based on many manufacturing-related factors. Thus, monitoring the cure process non-destructively in situ is key to manufacturing composite laminates to achieve the as-designed properties while balancing the cycle time reduction. The current work presents a pulse-echo ultrasound method to correlate the acoustic waveform to the thermoset resin cure state and the instantaneous structural properties, specifically the resin storage and loss moduli. This latter information provides a fabricator knowledge of when a part can be successfully demolded, allowing for optimizing part cycle times. The present paper provides the results for the neat resin specimen and fiberglass specimen impregnated with the same resin system. The results provide a direct correlation between the acoustic and the viscoelastic properties. Interestingly, it is noted that there is a direct correlation between the peak signal attenuation and the peak gelation of the material, thus providing a means to predictively schedule the demolding time while maintaining proper curing cycles.

Source: Applied Sciences

DOI: 10.3390/app16031473

Authors: Savannah M. Rose, Jackson C. Wilkins, Trevor J. Fleck, David A. Jack

Institution: Baylor University

Language: English

Topic: Ultrasonics and Acoustic Wave Propagation

Subfield: Mechanics of Materials

Field: Engineering

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $2,896

Funder: Baylor University