Role of Si substitution in modulating the coercivity and magnetic anisotropy in Fe3CoB2 nanocrystallites

Year: 2026

Type: article

Abstract: In this work, we report the impact of Si substitution on the structural and magnetic properties of Fe3CoB2 nanocrystallites as a rare-earth-free hard-magnet candidate. X-ray diffraction confirmed the formation of the tetragonal phase with an average crystallite size of ∼40 nm, while the transmission electron microscopy image revealed nanosized crystallites embedded in an amorphous matrix. Room-temperature Mössbauer spectra exhibited two sextets and two doublets, indicating magnetically ordered Fe sites in the tetragonal phase along with high-spin paramagnetic FeIII species in disordered regions. ZFC–FC magnetization curves displayed field-dependent blocking behavior, consistent with paramagnetic Fe species. Singular point detection measurements revealed a high anisotropy field of ∼10.7 kOe in the pristine Fe3CoB2, and systematically decreased with Si substitution. Magnetization measurements revealed a monotonic decrease in saturation magnetization with Si content, while coercivity was observed to increase, likely due to microstructural refinement. These results establish Fe3CoB2 as a rare-earth-free material with strong magnetic anisotropy, ideal for hard magnets.

Source: AIP Advances

DOI: 10.1063/9.0001045