Year: 2026
Type: article
Abstract: Influence of parallel hydrogen evolution reaction (HER) on morphology of zinc electrodeposits has been investigated. Zn was electrodeposited potentiostatically from the alkaline electrolyte at overpotentials both inside and outside the plateau of the limiting diffusion current density, and scanning electron microscopy (SEM) was used to characterize the resulting deposits. Holes originating from detached hydrogen bubbles were formed among the branchy, fern-like dendrites at overpotentials outside the plateau of the limiting diffusion current density, while HER was not detected at the overpotential inside the plateau. The overpotential of electrodeposition had no significant effect on the amount of hydrogen produced (the HER current efficiency was in the 17.7-19.1 % range), but it did affect the hole size. Depending on the overpotential of the electrodeposition, the size of holes was from several to about 100 mm, including those obtained by a coalescence of neighbouring hydrogen bubbles, and decreased with the increasing overpotential. The absence of inhibition of dendritic growth in spite of a high value of evolved hydrogen was attributed to Zn, which belongs to the group of normal metals characterized by high values of both the exchange current density and the overpotential for hydrogen evolution.
DOI: 10.5599/jese.3191
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: diamond
Award: G1446243131
OpenAlex ID: W7128036357