Abstract: With the growing clinical use of ion-releasing resin composites, their repairability has become an important consideration in minimally invasive restorative dentistry. Therefore, this study investigated the repair bond strength of a universal composite restorative to commercially available and experimental ion-releasing resin composite materials. Specimens (n = 8 per group) were produced from three commercially available ion-releasing composite materials (ACTIVA BioACTIVE-RESTORATIVE, Cention Forte, Beautifil II), one experimental ion-releasing resin composite containing 20 wt% bioactive glass fillers, and two conventional resin composites (3M Filtek Supreme XTE, Ceram.x Spectra ST), and aged by thermal cycling in artificial saliva (5000 cycles, 5–55 °C). Substrate surfaces were sandblasted (Al2O3, 50 µm), silanized (Monobond Plus), and repaired using adhesive (OptiBond FL) and universal resin composite (Ceram.x Spectra ST). After further thermal cycling, micro-tensile repair bond strength was assessed and analyzed using one-way ANOVA followed by Tukey’s post hoc test. Failure modes were determined by stereomicroscopy (25× magnification) and statistically compared among the groups. Highest mean repair bond strength values were obtained for ACTIVA BioACTIVE-RESTORATIVE, Beautifil II, and 3M Filtek Supreme XTE (53.8, 46.2, and 43.0 MPa, respectively), which did not differ significantly among each other. ACTIVA BioACTIVE-RESTORATIVE attained significantly higher bond strength than the experimental composite, Ceram.x Spectra ST, and Cention Forte, and showed the highest incidence of cohesive failures (40%). No significant bond strength differences were detected among Beautifil II, 3M Filtek Supreme XTE, experimental composite, Ceram.x Spectra ST, and Cention Forte (36.2–46.2 MPa). In conclusion, ion-releasing resin composites can be repaired with conventional universal composite and show repair bond strength values at least as high as those of conventional composite materials.
Source: Materials
DOI: 10.3390/ma19061076
Institutions: University of Zurich, University of Zagreb
Language: English
Subfield: Orthodontics
Field: Dentistry
Domain: Health Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W7135083294