Effect of composition on the micro-nano mechanical properties and crystal plasticity constitutive parameters of TNM-based TiAl alloys

Year: 2026

Type: article

Abstract: • The effects of Al content and Mo content on the hardness and elastic modulus of TNM-based TiAl alloys were systematically discussed. • The size-independent hardness value (H 0 ) is determined through nanoindentation analysis accounting for size effects, and the effects of Al content and Mo content on the H 0 value of TNM-based TiAl alloys were discussed. • The crystal plasticity constitutive parameters of γ and α 2 phase in TiAl alloys with different Al content and Mo content was calibrated by fitting the load–displacement curves of simulated and experimental data. • The effects of Al content and Mo content on the critical resolved shear stress (CRSS) of TNM-based TiAl alloys were discussed. This study combines nanoindentation and crystal plasticity finite element (CPFE) simulations to determine the micro-nano mechanical properties and constitutive parameters of γ and α 2 phases in TiAl alloys. Phase-specific parameters were successfully calibrated through inverse analysis, validated by excellent agreement between simulated and experimental curves. Both phases showed orientation-dependent hardness, and the γ phase also exhibited orientation-dependent elastic modulus. The intrinsic size-independent hardness H 0 was determined through indentation size effect analysis. As Al content increases from 43% to 45%, γ-phase hardness rises from 3.470 GPa to 4.625 GPa while α 2 -phase hardness increases from 5.801 GPa to 6.734 GPa, with corresponding critical resolved shear stress (CRSS) values increasing by 43% and 50%, respectively. Conversely, increasing Mo content from 0.5% to 1.5% enhances γ-phase hardness from 3.629 GPa to 4.851 GPa but reduces α 2 -phase hardness from 7.326 GPa to 6.052 GPa, while similarly elevating CRSS values by 43% and 50%. Further analysis reveals that Al content increase elevates γ-phase elastic modulus by14.3% but reduces α 2 -phase modulus by 8.7%, whereas Mo content increase significantly enhances α 2 -phase modulus by 2.6% without substantially affecting γ-phase modulus. This integrated approach provides quantitative insights into composition-dependent mechanical behavior of individual phases in TiAl alloys.

Source: Materials & Design

DOI: 10.1016/j.matdes.2026.115789

Authors: Bangqi Yin, Xiangyi Xue, Bin Tang, Kaidi Li, Jinshan Li

Institutions: Northwestern Polytechnical University, State Key Laboratory of Solidification Processing

Language: English

Topic: Intermetallics and Advanced Alloy Properties

Subfield: Mechanical Engineering

Field: Engineering

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $3,650

Funders: National Natural Science Foundation of China, Northwestern Polytechnical University, State Key Laboratory of Solidification Processing, National Key Research and Development Program of China