Abstract: In this work, a flexible and sustainable radar-absorbing material (RAM) based on porous carbon derived from raw Kraft black liquor was developed. The porous carbon filler was synthesized through a simple, eco-friendly one-pot polymerization route, thereby avoiding lignin extraction, purification, and chemical activation steps. Macroporosity was introduced by using poly(methyl methacrylate) microspheres as a hard template, yielding a lightweight carbon material with a foam-like morphology, low density, and high porosity. The carbon filler was incorporated into a silicone rubber matrix at different loadings (5–25 wt.%) to produce flexible composites. The structural, morphological, and textural properties of porous carbon were investigated by SEM, EDX, Raman spectroscopy, nitrogen adsorption, and mercury porosimetry. The electromagnetic properties of composites were measured in the X-band (8.2–12.4 GHz) using a vector network analyzer. The mechanical behavior was evaluated through Young’s modulus. The results show that increasing filler content enhances dielectric losses and attenuation capability. Among all composites, the sample containing 20 wt.% of porous carbon exhibited the best electromagnetic performance, achieving a reflection loss of −42.3 dB at 10.97 GHz with a thickness of 2.43 mm, corresponding to an absorption efficiency of 99.99%. This performance is attributed to a favorable combination of impedance matching and quarter-wavelength cancellation effects. The developed sustainable, lightweight, and flexible composites demonstrate potential as low-cost RAM for aerospace and electromagnetic interference mitigation applications.
Source: Processes
DOI: 10.3390/pr14071082
Language: English
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,896
Award: G7799327175
OpenAlex ID: W7141054205