Preparation and Properties of a Xanthoceras sorbifolium Bunge Oil-Based Adhesive for Plywood

Year: 2026

Type: article

Abstract: Conventional adhesives for plywood are mostly derived from petroleum-based materials and commonly suffer from formaldehyde emission, posing threats to the environment and human health. In this study, a renewable resource, Xanthoceras sorbifolium Bunge oil, was used as the raw material. A high-performance bio-based adhesive was successfully prepared by synthesizing Xanthoceras sorbifolium Bunge oil dimethacrylate (MXOEA) as a reactive diluent, blending it with acrylated epoxy Xanthoceras sorbifolium Bunge oil (AEXO), and introducing 2-isocyanatoethyl methacrylate (IEM) to enhance crosslinking. The effects of the MXOEA/AEXO ratio and the IEM addition level on the properties of the adhesive and the resulting plywood were systematically investigated. The results showed that when the mass ratio of AEXO to MXOEA was 3:7, and the IEM content was 10%, the adhesive exhibited the best bonding performance: the resulting plywood achieved a modulus of rupture of 68.85 MPa, a modulus of elasticity of 8086 MPa, and dry and wet bonding strengths of 3.21 MPa and 2.32 MPa, respectively. Mechanistic analysis indicated that the introduction of IEM moderately reduced the viscosity of the adhesive system. Meanwhile, the isocyanate groups in IEM reacted with the hydroxyl groups on the wood surface, forming a chemical crosslinking structure at the adhesive-wood interface, which is considered one of the reasons for the improved mechanical properties of the plywood. This study provides a formaldehyde-free, high-performance bio-based adhesive derived from Xanthoceras sorbifolium Bunge oil for the field of wood-based composites.

Source: Coatings

DOI: 10.3390/coatings16040463