Impedimetric Analysis of the Photocatalysis-Assisted Response of Patterned TiO2|ITO Electrodes Exposed to Artificial Sweat
Year: 2026
Type: article
Abstract: We report the fabrication and electrochemical characterization of TiO2-based impedimetric sensors for the analysis of artificial sweat compositions. Two-electrode topologies were patterned on indium tin oxide (ITO) substrates: an interdigitated electrode (IDE) configuration and a Hilbert fractal electrode (HFE) geometry. TiO2 thin films with thickness up to 350 nm were deposited by dip-coating and evaluated as photoactive sensing layers. The impedimetric response of the sensors was investigated by electrochemical impedance spectroscopy in artificial sweat with composition varied in terms of ionic content (0–100 mM Na+) and organic content (2.5–30 mM lactic acid and 5–50 mM urea). Regardless of TiO2 thickness, the high-frequency response is predominantly governed by electrode topology, with the HFE design exhibiting up to 2.5-fold higher modulation compared to the IDE configuration. Under UV illumination, a low-frequency, photo-assisted response emerges, influenced by the TiO2 layer thickness and primarily sensitive to the organic components of the solution, particularly lactic acid. These results suggest that frequency-resolved impedance measurements in TiO2|ITO structures may enable partial differentiation between ionic conductivity and organic contributions in sweat, providing a promising basis for multi-parameter sweat analysis.
Source: Sensors
DOI: 10.3390/s26082365
Institution: Technical University of Sofia
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W7154169533
FWCI:
Cites:
Cited by:
Related to: