Fabrication of Dual-Phase Mixed Conductor Four-Channel Hollow Fiber Membrane for Hydrogen Separation

Year: 2026

Type: article

Abstract: Perovskite mixed proton–electron hydrogen-permeable membranes have been widely applied in the field of membrane separation due to their 100% selectivity for hydrogen separation. La5.5WO11.25-δ-La0.87Sr0.13CrO3-δ (LWO-LSF) four-channel hollow fiber membranes were prepared by the phase inversion and sintering technique using a one-step thermal processing (OSTP) approach. The effects of temperature, feed gas concentration, sweep gas flow, permeation mode, and water vapor on hydrogen flux were systematically investigated. At 900 °C, the hydrogen permeation flux of 50% H2/N2 feed from the shell side to the lumen side was 0.613 mL·min−1·cm−2, which was 62.59% higher than that from the lumen side to the shell side. The enhanced hydrogen permeation performance is attributed to the lower gas mass transfer resistance under shell-side feeding. Under humidified conditions on the sweep side, the hydrogen flux increased by an additional 3.42%. The presence of water vapor increased the number of proton carriers, effectively enhancing proton–electron-coupled transport and thereby increasing the hydrogen permeation flux.

Source: Membranes

DOI: 10.3390/membranes16050158

Authors: Doudou Jia, Haonan Wang, Zhengkun Liu, Guangru Zhang, Wanqin Jin

Institutions: Nanjing Tech University, State Key Laboratory of Materials-Oriented Chemical Engineering

Language: English

Topic: Advancements in Solid Oxide Fuel Cells

Subfield: Materials Chemistry

Field: Materials Science

Domain: Physical Sciences

SDG: Affordable and clean energy

Open Access status: gold

Estimated APC paid: $2,654