A High-Phosphogypsum Multi-Solid-Waste Cementitious Binder for Backfill: Cross-Scale Insight into Pore Structure and Strength Development

Year: 2026

Type: article

Abstract: Phosphogypsum (PG) is an industrial solid waste whose use in cementitious materials is limited by strength reduction at high dosages. This study evaluated a clinker-free multi-solid-waste binder containing 40 wt.% PG for cemented paste backfill using steel slag powder (SSP) and granulated blast-furnace slag (GBFS) as co-binders, with phosphate mine tailings and slime as aggregates. Uniaxial compressive strength (UCS), X-ray diffraction, scanning electron microscopy, and nuclear magnetic resonance were combined with image-based pore-structure sensitivity analysis to examine the relationships among hydration products, pore evolution, and strength development. The results showed that AFt and C-S-H-like gels were associated with pore refinement and strength gain. All mixtures reached UCS values above 0.5 MPa at 7 days and 1.0 MPa at 28 days. The A2 mixture achieved the highest 7-day UCS of 0.8 MPa, whereas A1 showed the highest 28-day UCS of 1.6 MPa. Porosity, pore probability entropy, and fractal dimension were negatively correlated with UCS, with pore probability entropy showing the highest sensitivity to 7-day strength. These findings support the use of high-PG clinker-free binders for targeted phosphate-mine backfill.

Source: Materials

DOI: 10.3390/ma19102156

Authors: Jianhua Hu, Xingjian Jiang, Fengwen Zhao, Zhi Yu, Ying Zhou, Dehua Wang

Institution: Fuzhou University

Language: English

Topic: Concrete and Cement Materials Research

Subfield: Civil and Structural Engineering

Field: Engineering

Domain: Physical Sciences

SDGs: Responsible consumption and production, Industry, innovation and infrastructure

Open Access status: gold

Estimated APC paid: $3,137