A Novel Cutting Force Prediction Model and Damage Analysis of Laser-Assisted Cutting CFRP at 135° Cutting Angle
Year: 2026
Type: article
Abstract: Carbon fiber-reinforced polymer (CFRP) composites are widely employed in the aerospace industry due to their excellent properties such as high specific strength and corrosion resistance. However, the delamination and tearing of composites are prone to occur in the machining of CFRP, which significantly affect its performance. The existing laser-assisted cutting model generally simplifies the machining process into high-temperature conventional cutting, and only reflects the thermal effect by modifying the material parameters. The core selective ablation characteristics of laser–CFRP interaction are completely ignored, and the unique mechanical behavior of bare fiber under a large cutting angle is not modeled, and the quantitative correlation between cutting force evolution and machining damage is lacking. In this study, an innovative method of partially exposing fibers is proposed to simulate laser-assisted machining. A micromechanical model is developed to analyze the removal mechanisms of different phases during CFRP processing, and a cutting force prediction model from the micro to macro scale is also established. At the micro-scale, a micromechanical model for fiber cutting in orthogonal machining of CFRP is constructed based on the elastic foundation beam theory. The results show that the proposed cutting force prediction model has high reliability, and the relative error between the predicted value and the experimental measured value is only 7.81%~8.99%. All experiments were repeated three times. Statistical analysis showed that the repeatability of the results was excellent. Compared with conventional cutting, laser-assisted cutting fundamentally changed the failure mode of the fiber from matrix-constrained crushing fracture to controllable free-end large-deflection bending fracture. This transformation leads to a smoother and more regular fiber fracture surface, which effectively inhibits fiber breakage, matrix tearing, and fiber–matrix interface debonding. Quantitative analysis confirms that under laser-assisted processing conditions, the matrix tearing length is positively linearly correlated with the cutting depth, cutting speed, and bare fiber length.
Source: Crystals
Institution: Shenyang Aerospace University
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,534
Award: G5519709879
OpenAlex ID: W7161980511