Hydrothermally assisted sintering of calcium hydroxide sputtering targets: a route to quantum-grade CaO thin films

Year: 2026
Type: article
Abstract: In this report, we demonstrate dense polycrystalline calcium hydroxide ceramics fabricated by hydrothermally assisted sintering—often referred to as cold sintering—to produce high-purity calcium hydroxide targets for calcium oxide thin film deposition. Calcium hydroxide ceramics exhibit up to 98% relative density without thermal dehydration when sintered at temperatures between 100 and 300 °C with 400 MPa applied uniaxial pressure for 1 hour. The brucite phase is preserved in calcium hydroxide targets sintered at all temperatures. Small equivalent fractions of calcium carbonate are present in both the calcium hydroxide precursor powder and final targets suggesting minimal additional carbonate production during formation and densification. Microstructure evolution during densification is documented by scanning electron microscopy (SEM), indicating both mass transport and plastic deformation densification mechanisms. The hydrothermal-assisted sintering process is scaled up to produce 2-inch-diameter calcium hydroxide targets suitable for sputter deposition. We also report epitaxial calcium oxide film deposition from these targets on r -plane sapphire substrates. (002)-oriented epitaxial films are achieved with a time-stable deposition rate of 1.2 nm per minute. We note that energetic bombardment during growth can be substantial, necessitating an off-axis sputter cathode geometry.
DOI: 10.1007/s10853-026-13788-4
Language: English
Open Access status: hybrid
Estimated APC paid: $3,590
OpenAlex ID: W7163192315
FWCI:
Cites:
Cited by:
Related to: