Structural and electrical characterization of Hf0.5Zr0.5O2 thin films crystallized by rapid thermal annealing

Year: 2026

Type: article

Abstract: The effects of rapid thermal annealing (RTA) temperature on the structural and electrical properties of 10 nm-thick Hf 0.5 Zr 0.5 O 2 (HZO) thin films were investigated. Structural analyses revealed that the films remained largely amorphous at low annealing temperatures and crystallized above 600 °C, where the ferroelectric orthorhombic phase became dominant. At higher temperatures, the formation of the monoclinic phase was also observed. Electrical characterization demonstrated a strong dependence of ferroelectric behavior on annealing temperature. Films annealed near 600 °C exhibited the most stable ferroelectric domains, strongest polarization switching, and most distinct hysteretic behavior, whereas higher temperatures led to a gradual degradation of the electrical response. These results indicate that an annealing temperature around 600 °C provides the optimum condition for achieving enhanced ferroelectric performance in HZO thin films.

Source: Han-guk hyeonmigyeong hakoeji/Applied microscopy

DOI: 10.1186/s42649-026-00141-x

Authors: Jucheol Park, Yeong Gyeong Park, Min-Ho Kang, Myung-Keun Lee, Moon Seop Hyun

Institutions: Gumi Electronics & Information Technology Research Institute (South Korea), National NanoFab Center

Language: English

Topic: Ferroelectric and Negative Capacitance Devices

Subfield: Electrical and Electronic Engineering

Field: Engineering

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $2,590

Funders: National Research Foundation, National Research Foundation of Korea