Effect of Sintering Temperature on Protective Oxide Formation and Corrosion Resistance of Ti-6Al-4V in Na2SO4–NaCl Salt Mixtures
Year: 2026
Type: article
Abstract: This study investigates the effect of sintering temperature on the hot-corrosion behavior of Ti-6Al-4V alloy in a molten salt environment. Samples were sintered at 800 °C, 900 °C, 1000 °C and 1100 °C, then exposed to the Na2SO4—25%NaCl for 300 h at 650 °C. The corrosion kinetics were evaluated by measuring the mass change in the specimens, and the results were correlated with their corresponding corrosion rates. The results show that the sintering temperature drives corrosion kinetics by influencing the sample density and grain size. The sample sintered at 900 °C shows a low corrosion rate due to its refined microstructure. This refined microstructure provides a high grain boundary density, which serves as a diffusion path and enables the formation of a dense, protective Al2O3–TiO2 layer, as confirmed by XPS. In contrast, the sample sintered at 800 °C exhibits high porosity, resulting in an initial weight loss due to molten-salt penetration and evaporation of volatile metal chlorides. The samples sintered at 1000 °C and 1100 °C exhibit coarsened grains, leading to a thicker, brittle oxide layer and severe delamination, which in turn result in high corrosion rates. The results show that optimizing the sintering temperature to around 900 °C would enhance hot-corrosion resistance in salt-contaminated environments.
DOI: 10.3390/cmd7020038
Institution: Vellore Institute of Technology University
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,207
OpenAlex ID: W7165016526