Integrated multi-assessment and structural performance index framework for stacking-sequence optimisation of natural fibre reinforced laminates
Year: 2026
Type: article
Abstract: Natural fibre-reinforced polymer composites (NFRPCs) are sustainable alternatives to synthetic laminates; conversely, their structural reliability is influenced by type of fibre, fibre orientation and stacking architecture. In this work, ten sample laminate configurations (S1-S10) with Flax (F), Hemp (H), and Kenaf (K) fibres were fabricated using a hand lay-up method with single-layer (SL), double-layer (DL), and alternating-layer (AL) sequences under 0/90° and ± 45° orientations. Mechanical properties, namely tensile, flexural, and compressive strengths, were experimentally evaluated. The double-layer 0/90° configuration (S7) demonstrated optimal mechanical performance, achieving Tensile, Flexural, and Compressive strengths of 57.13 MPa, 60.50 MPa, and 638.63 MPa, respectively. Shifts in the laminate orientation from 0/90° to ± 45° resulted in tensile reductions of up to 54%, thereby enhancing shear-dominated stress redistribution. A mechanics-informed Structural Performance Index (SPI) framework was developed, incorporating normalised tensile, flexural, and compressive responses into application-specific structural indicators. The SPI-based evaluation recognised S7 as the best arrangement for structural and crash-dominant scenarios (SPI = 0.99), whereas kenaf-dominant laminates (S5) were recommended for the stiffness-oriented applications. The proposed SPI methodology delivers a decision tool that associates experimental characterisation and reliability-driven laminate selection for multi-axial engineering applications.
Source: Scientific Reports
Institution: SASTRA University
Language: English
Subfield: Polymers and Plastics
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,690
OpenAlex ID: W7166584550
FWCI:
Cites:
Cited by:
Related to: