Internal Degradation of 2.5D C/SiC Composites Under Continuous-Wave Laser Irradiation: Experiments and Phase-Selective Modelling

Year: 2026

Type: article

Abstract: Surface recession can underestimate laser-induced damage in 2.5D C/SiC composites because thermochemical degradation extends beneath the visible pit. Infrared thermography and micro-CT data from six laser conditions (400–1600 W·cm−2, 3–12 s), together with SEM/EDS observations, were reanalysed using a layered phase-selective model tracking C, SiC and SiO2 evolution. For the four conditions with resolvable damage, the internal degradation front lay 0.84–1.07 mm below the recession surface. At 800 W·cm−2, the 0.02 mm difference between the 6 and 12 s front depths was below the 25 μm voxel size and within specimen uncertainty. The calibrated model matched rear-centre peak temperatures with a mean absolute percentage error of 4.37%, although larger transient discrepancies remained. Temperatures sampled at the measured front coordinates ranged from 2890 to 3080 K. Relative to 800 W·cm−2 for 12 s, the 1600 W·cm−2, 6 s condition caused greater near-surface SiC consumption and solid-mass loss, while the maximum retained SiO2 density decreased from approximately 360 to 180 kg·m−3. These results distinguish geometric recession from internal degradation and support experimental-front mapping and mechanistic interpretation. The mapped states are condition-specific and do not constitute an independently predicted front criterion.

Source: Materials

DOI: 10.3390/ma19163558

Authors: Chuntong Liu, Renke Wang, Yuwei Lv, Yubin Shi

Institutions: PLA Rocket Force University of Engineering, Northwest Institute of Nuclear Technology

Language: English

Topic: Advanced ceramic materials synthesis

Subfield: Ceramics and Composites

Field: Materials Science

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $3,137

Funder: State Key Laboratory of Laser Interaction with Matter