Filament Heating Voltage Effects on Cathode Operation and Weld Formation in Thin-Sheet Ti-6Al-4V Electron-Beam Welding
Year: 2026
Type: article
Abstract: Filament heating voltage governs thermionic electron emission in electron-beam guns, but its influence on weld formation under fixed electron-beam welding settings has received limited quantitative investigation. In this study, Ti-6Al-4V thin sheets were welded at filament heating voltages of 2.8–3.4 V, while the accelerating voltage, beam current, focusing current, and welding speed were kept constant. Weld cross-sections were characterized experimentally, and the resulting thermal process was analyzed using a simplified cathode-emission calculation and finite element thermal analysis. A clear change in weld penetration behavior was observed within approximately 3.2–3.3 V. The weld aspect ratio increased from approximately 0.4 below this region to approximately 0.6 at 3.3 V and further to approximately 0.63 at 3.4 V. Concurrent changes in the required bias voltage, calculated equivalent cathode area, and weld geometry were consistent with a change toward a more stable cathode operating condition. The weld-geometry changes were also consistent with a change in the effective beam-energy distribution, although the beam profile was not measured directly. These results show that filament heating voltage should be treated as an independent equipment-side control variable even when the main electron-beam welding settings remain unchanged. Although the specific transition range depends on the electron gun, beam-current setting, and cathode condition, the electrical-response-based identification approach may provide a practical method for identifying the filament operating range when direct beam diagnostics are unavailable.
DOI: 10.3390/jmmp10080309
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,172
OpenAlex ID: W7203917091