Reversible Electrolyte-Supported Solid Oxide Cells Fabricated by Aqueous Mold-Casting
Year: 2026
Type: article
Abstract: Reversible Solid Oxide Cells (rSOCs) are highly efficient energy conversion systems for power generation in fuel cell mode (SOFC) and energy storage in electrolysis mode (SOEC). These devices are typically manufactured through multi-step processing routes based on conventional functional ceramic fabrication techniques, such as tape-casting, extrusion, screen-printing and spraying. In this work, an alternative mold-casting approach is proposed for the fabrication of planar electrolyte-supported rSOCs. Electrolytes made of 8 mol% yttria-stabilized zirconia (YSZ) were prepared via an aqueous gel-casting process using agarose as the gelling agent. The casting molds were fabricated by 3D printing with polylactic acid (PLA) filament. Dense electrolytes with well-controlled geometries were successfully obtained. Complete cells were produced using porous Ni–YSZ as a fuel electrode and porous lanthanum strontium manganite–YSZ. The cells were microstructurally characterized, and their electrochemical performance was evaluated under both SOFC and SOEC operating conditions at 800–900 °C. At 900 °C, the cell achieved a peak power density of 220 mW cm−2 in fuel cell mode and an injected current density of 340 mA cm−2 at 1.3 V in electrolysis mode. Mid-term galvanostatic testing in SOFC mode at 850 °C for 400 h demonstrated good durability and structural stability of the fabricated cells. After the initial stabilization period, the cell exhibited a low degradation rate of 3 mV kh−1.
Source: Energies
DOI: 10.3390/en19173964
Institution: Universitat Politècnica de Catalunya
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W7204069732