Mechanical and thermal performance of epoxy nanocomposites reinforced with teak-sawdust-derived carbon nanospheres
Year: 2026
Type: article
Abstract: A polymer matrix nanocomposite was fabricated using sustainably derived, porous carbon nanospheres (CNS), a green nanomaterial synthesized from bio-waste teak-wood sawdust (TW). The CNS were prepared through a one-step pyrolysis process at three different temperatures – 500, 700, and 1000 °C. Scanning electron microscopy revealed that the CNS obtained at 1000 °C (TW1000) exhibited the smallest average particle size, ranging from 40 to 50 nm, along with a higher degree of carbonization. These TW1000 CNS were incorporated into a commercial-grade LY5052 epoxy matrix at varying loadings of 0.05, 0.1, and 0.3 wt%. This work investigates the use of teak-wood-derived porous carbon nanospheres as sustainable nanofillers for epoxy composites at low filler loadings (0.05–0.30 wt%), with particular emphasis on their performance under elevated-temperature conditions. The composites were evaluated through tensile testing to assess their mechanical performance and structural integrity. The 0.1 wt% TW1000 CNS/epoxy composite demonstrated the best combination of tensile strength and ductility, showing a significant improvement compared to the neat epoxy. The composite also retained its mechanical properties after exposure from room temperature to 300 °C for one hour at different intervals, indicating excellent thermal resistance. Furthermore, thermogravimetric analysis confirmed the composite’s thermal stability up to 300 °C, highlighting its suitability for high-temperature and multifunctional applications.
Source: Discover Materials
Institutions: Christ University, Dayananda Sagar University
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,590
Funder: Dayananda Sagar University
OpenAlex ID: W7204139188
FWCI:
Cites:
Cited by:
Related to: