High‐Temperature Corrosion of Unpassivated Carbon Steel in Simulated Boiler Water: Electrochemical Thresholds and Mechanisms for Chloride and Sulphate Contamination

Year: 2026

Type: article

Abstract: ABSTRACT Cl − and SO 4 2− in boiler water pose a significant threat to carbon steel boiler tube integrity, yet their corrosion mechanisms at industrial temperatures remain poorly characterized. This study quantifies corrosion thresholds and mechanistic roles of these contaminants for unpassivated SA210‐A1 carbon steel in simulated all‐volatile treatment (AVT) boiler water at 310°C and 10.3 MPa, using in situ linear polarization resistance measurements (LPR) supported by FactSage modeling. The corrosion threshold for SO 4 2− was 1.5–3 times higher than for Cl − , supporting industry heuristics. Mechanistic analysis indicates that Cl − lowers solution pH, increasing iron solubility, while SO 4 2− reduction to H 2 S is thermodynamically favoured under high‐temperature reducing conditions and could provide an additional cathodic pathway. The initial chemical form of the contaminants governed combined behaviour: ammonium salts raised the combined threshold above that of Cl − alone, while mineral acids lowered it, better representing acidic, deposit‐controlled boiler conditions. These findings establish a mechanistic baseline and relative threshold relationships to inform water chemistry guidelines.

Source: Materials and Corrosion

DOI: 10.1002/maco.70283

Authors: Benjamin A. Loder, William G. Cook

Institution: University of New Brunswick

Language: English

Topic: Corrosion Behavior and Inhibition

Subfield: Materials Chemistry

Field: Materials Science

Domain: Physical Sciences

SDG: Clean water and sanitation

Open Access status: hybrid

Estimated APC paid: $3,540