Effect of surface sealants on microleakage of Class II restorations after thermocycling and long-term water storage.
Year: 2011
Type: article
Abstract: PURPOSE: To evaluate interface degradation leading to marginal microleakeage in Class II restorations that had received an application of surface sealant at the tooth/restoration interface or not. MATERIALS AND METHODS: Eighty bovine incisors were used, and the teeth were split obliquely, 10 mm from the amelodentinal proximal junction, and finished with water abrasive papers to obtain a smooth, flat incisal surface. Cavities were made to simulate Class II preparations (8 mm high, 4 mm wide and 1.5 mm deep), and the restorations were performed with a composite resin. Teeth were then randomly allocated into 8 groups according to the surface sealant (none, Fortify, Single Bond 2, or Scothbond MP Plus) and aging process (none or thermocycling and storage for 6 months). Microleakage was then evaluated using a dye penetration method immediately after the restoration or after aging. The samples were triturated and assessed by spectrophotometer. RESULTS: Microleakage was statistically similar in all groups when assessed immediately after the restorative procedure. After aging, teeth sealed with Fortify presented better results than the other groups. CONCLUSION: Aging causes interface degradation and increased microleakage. Surface sealant can reduce these effects and decrease microleakage in Class II restorations.
Source: PubMed
DOI: 10.3290/j.jad.a19242
Institution: Universidade Estadual de Campinas (UNICAMP)
Language: English
Subfield: General Dentistry
Field: Dentistry
Domain: Health Sciences
Open Access status: green
OpenAlex ID: W190078116