Thermally Grafting Aminosilane onto Kenaf-Derived Cellulose and Its Influence on the Thermal Properties of Poly(Lactic Acid) Composites
Year: 2013
Type: article
Abstract: The effects of thermally grafting hydrolysed 3-aminopropyltriethoxysilane (APS) onto kenaf-derived cellulose and the influence of incorporating them into poly(lactic acid) (PLA) were investigated.Composites containing 30 wt.% cellulose (C) and silane-grafted cellulose (SGC) were melt-blended into PLA before being hot pressed into 0.3-mm films.The silane grafting of cellulose was confirmed via Fourier transform infrared spectroscopy (FTIR) with the presence of Si-O-Si, Si-O-cellulose, -Si-C-, and Si-O-C bonds, and -NH 2 groups despite post ethanol washing.Using thermogravimetric analysis (TGA), it was determined that the thermal stability of the cellulose improved by 8 o C after silane grafting.As for the composites, PLA/SGC improved the thermal stability by 12 o C as compared to PLA/C.From differential scanning calorimetry (DSC), adding C into PLA slightly reduced the glass transition temperature, T g , of the PLA from 59 o C to 57 o C, which remained unchanged with silane grafting.PLA displayed double melting peaks from its meltrecrystallization behaviour.While the final melting temperature at 150 o C was not affected, incorporating C and SGC influenced the intensity of the melting peaks.The significant reduction in crystallisation temperature from 113 o C to 102 o C and 105 o C, and the increase in crystallinity by almost two fold, indicated that cellulose was an effective nucleating agent.
Source: BioResources
Institution: Universiti Putra Malaysia
Language: English
Subfield: Polymers and Plastics
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,452
Funder: Universiti Putra Malaysia
OpenAlex ID: W1990753164