A NiO/TiO2 junction electrode constructed using self-organized TiO2 nanotube arrays for highly efficient photoelectrocatalytic visible light activations
Year: 2010
Type: article
Abstract: One dimensional (1D), self-organized TiO2 nanotube arrays are known to have excellent charge transport properties and a NiO/TiO2 junction is efficient in separating electron–hole pairs. This paper describes the synthesis of a NiO/TiO2 junction electrode constructed using self-organized TiO2 nanotube arrays combining the above two properties. The self-organized TiO2 nanotube arrays used in this study were prepared by anodizing titanium films, which resulted in closely packed n-type TiO2 tubes with an inner pore diameter of 60–90 nm, a wall thickness of approximately 15 nm and a length of 600 nm. The NiO/TiO2 junction was synthesized by electroless plating and annealing which resulted in TiO2 nanotube arrays coated with a layer (about 200 nm in thickness) of NiO particles (20–40 nm). The resulting NiO/TiO2 junction electrode enabled us to obtain an enhanced photocurrent (3.05 mA cm−2) as compared with a TiO2 electrode based on TiO2 nanotube arrays (0.92 mA cm−2) under AM 1.5 G (100 mw cm−2) at a bias of 0.65 V.
Language: English
Field: Energy
Domain: Physical Sciences
Open Access status: bronze
OpenAlex ID: W2000392951