Effect of Milling Time on the Formation of NiAl Nanostructure Intermetallic Produced by the Mechanical Alloying Process
Year: 2013
Type: article
Abstract: In the present study, NiAl nanostructure intermetallic produced by mechanical alloying process was investigated. Pure Al and Ni powders with the ratio of 50 at.% were mixed and milled in a planetary ball mill for different milling times in the range of 8 to 128 hours. The milled powder particles were investigated by XRD technique and scanning electron microscope. Williamson-Hall equation was employed to calculate lattice strains and crystallite sizes. The results showed that NiAl intermetallic formed after some milling times. The observation of flame or explosion in the vial just after the uncovering of it, in some cases, showed intense interaction between Al and Ni atoms after homogenization during milling. After longer milling time no flame and explosion was observed while NiAl intermetallics had been formed. Therefore, NiAl intermetallics were formed under different conditions with different structures and properties. The crystal sizes of obtained NiAl particles were less than 10 nm. The hardness changes in particles and also their internal strains were affected by milling operation at early stages of milling but they were mainly affected by transformation process of (Ni,Al) solid solution into intermetallic NiAl at longer milling times.
Source: Advanced materials research
Institution: Shahid Bahonar University of Kerman
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
OpenAlex ID: W2005377492