Studies on Martensite Transformation in a Metastable Austenitic Cr-Mn Stainless Steel
Year: 2013
Type: article
Abstract: The influences of the heating rate and annealing duration on martensite formation and its reversion to austenite have been investigated in a 60% cold-rolled metastable high-manganese austenitic Type 204Cu stainless steel. A Gleeble 3800 thermomechanical simulator was used for dilatometric measurements. Cold-rolled steel pieces were either heated up to 1000 °C at various heating rates between 5 °C/s and 150 °C/s followed by quenching to room temperature, or heated and held at temperatures in the range of 450 620 °C for different durations between 0.1 600 s. In heating experiments, dilatation curves revealed an expansion of a specimen starting around 550 °C followed by contraction, both processes depending on the heating rate. These dimensional changes could be correlated to the formation and reversion of a ferromagnetic phase, α-martensite. Some martensite was also formed during isothermal holding in connection with tempering of the pre-existing α-martensite before the following reversion, as established by magnetic measurements. Tempering of martensite was revealed by microhardness behaviour, X-ray diffraction analysis and transmission electron microscopy.
Source: Materials science forum
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Funder: Tekes
OpenAlex ID: W2016897446