SOLUTION COMBUSTION SYNTHESIS AND CHARACTERISTICS OF NANOSCALE MgO POWDERS
Year: 2011
Type: article
Abstract: Nanoscale MgO powders were fabricated via a microwave-induced solution combustion process using Mg(NO3)2 and starch as starting materials. Effects of the relative fuel-to-oxidant ratios (φe = 1.1, 1.0, 0.9 and 0.8, respectively) on characteristics of MgO nanoparticles were also investigated. The XRD analysis discloses that MgO nanocrystalline are successfully synthesized and the crystalline size of MgO increases remarkably with increasing of φe from 0.8 to 1.1. TEM images reveal that nanoporous agglomerates of MgO nanocrystalline are formed in the powders. Experimental results show that the average particles’ size of the powders decreases significantly as φe increases from 0.8 to 1.1. However, the powders from the precursors with φe equal to 1.0 exhibit larger specific surface area as compared the other powders.
Authors: JIAHAI BAI, FANTAO MENG, CHUNCHENG WEI, YUNXIA ZHAO, HUIHUI TAN, JUNCHENG LIU
Institution: Shandong University of Technology
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: green
OpenAlex ID: W2302786338