DIP-COATING SENYAWA KALSIUM FOSFAT DARI BATU KAPUR BUKIT TUI DENGAN VARIASI RATIO MOL Ca/P MELALUI METODE SOL-GEL
Year: 2016
Type: article
Abstract: Preparation of Dip-Coating Calcium Phosphate via sol-gel method using natural limestone Bukit Tui as calcium precursors and diammonium hydrogen phosphate as phosphorus precursors with various Ca/P mol ratio has been investigated. Etanol was used as solvent and DEA (dietanolamine) as stabilizing agent. Powder were prepared by calcinated the sol at 950 o C. The results characterized by Fourier Transform Infra-red, X-Ray diffraction and Scanning Electron Microscopy. FTIR results showed that the vibration form was PO 4 3- , P 2 O 7 4- , O-H and CO 2 . X-Ray Diffraction (XRD) patterns of powder with various Ca/P mol ratio showed that the product of calcium phosphate was Ca 2 P 2 O 7 and also found the hydroxyapatite Ca 10 (PO 4 ) 6 (0H) 2 in Ca/P ratio mol 1,7. Scanning Electron Microscopy (SEM) images of powder calcium phosphate revealed that their morphology were spheric and homogen. The coating process was done at glass substrate with coating speed 20 cm/min by calcinations at 400 o C. . X-Ray Diffraction (XRD) patterns of thin layer showed that the product was Ca 2 P 2 O 7 and Scanning Electron Microscopy (SEM) images of thin layer revealed that their morphology were bulk. Key words; natural limestone, calcium phosphate, hydroxyapatite, sol-gel, dip-coating
DOI: 10.31958/js.v7i1.123
Author: Lia Anggresani
Institution: Sekolah Tinggi Ilmu Kesehatan Harapan Ibu Jambi
Language: Indonesian
Subfield: Biomedical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W2772321941