Abstract: Atmospheric plasma spraying (APS) was taken to fabricate the NiCrAlY coating. The corrosion-wear properties of NiCrAlY coating was measured respectively under deionized water, artificial seawater, NaOH solution and HCl solution. Experimental results presented that the as-sprayed NiCrAlY coating consisted of Ni3Al, nickel-based solid solution, NiAl and Y2O3. In deionized water, the coating with the lowest corrosion current density (icorr) of 7.865 × 10−8 A/cm2 was hard to erode. Meanwhile, it presented a lower friction coefficient and the lowest wear rate. In HCl solution, NiCrAlY coating gave the highest corrosion current density (icorr) of 3.356 × 10−6 A/cm2 and a higher wear rate of 6.36 × 10−6 mm3/Nm. Meanwhile, the emergence of Al(OH)3 on the coating surface could reduce the direct contact between the counter ball and sample effectively, which was conducive to the lowest friction coefficient of 0.24.
Source: Materials
DOI: 10.3390/ma13081864
Institutions: Xi'an Jiaotong University, Lanzhou City University
Language: English
Subfield: Surfaces, Coatings and Films
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,112
Award: G4442724438
OpenAlex ID: W3016325901