In-situ X-ray radiography of twinned crystal growth of primary Al13Fe4

Year: 2020

Type: article

Abstract: The faceted growth of primary Al13Fe4 intermetallic compounds was studied using in-situ X-ray radiography in a solidifying Al-3Fe alloy. Microscopic twins were frequently observed in the growing intermetallics and were confirmed by post-solidification electron backscatter diffraction. A twin plane re-entrant growth mechanism was suggested, where repeated formation of re-entrant corners facilitated crystal growth along a preferential direction, forming elongated plates. In contrast, for intermetallics where this preferential growth was constrained by surrounding crystals, formation of layered twins perpendicular to the preferential direction was promoted and led to lower aspect ratios, known to be less deleterious to tensile properties.

Source: Scripta Materialia

DOI: 10.1016/j.scriptamat.2020.04.010

Authors: S. Feng, Y. Cui, E. Liotti, A. Lui, C.M. Gourlay, P.S. Grant

Institutions: University of Oxford, Imperial College London

Language: English

Topic: Solidification and crystal growth phenomena

Subfield: Materials Chemistry

Field: Materials Science

Domain: Physical Sciences

Open Access status: hybrid

Estimated APC paid: $3,000

Funder: Engineering and Physical Sciences Research Council