Adhesively bonded CFRP/Al joints: Influence of the surface pretreatment on corrosion during salt spray test
Year: 2021
Type: article
Abstract: The objective of this study was to investigate the influence of different surface pretreatments on the aging behavior of adhesively bonded carbon fiber reinforced polymers/Al joints in a standardized salt spray environment. Therefore, the bonding surfaces were acetone‐cleaned or laser‐pretreated by near‐infrared laser radiation. The pretreated surfaces were examined using optical microscopes, roughness measurements, and infiltration tests. Mechanical testing of the joints was performed in the unaged state and after five aging durations from 120 to 1440 h. The acetone‐cleaned specimens lose a maximum 20% of their initial average shear strength of 22 MPa after aging up to 1440 h. In contrast, the fracture patterns of the laser‐pretreated samples show corrosive degradation after 720 h, indicating galvanic coupling and crevice corrosion. This leads to a significant decrease in shear strength up to 50% after 1440 h of aging. Therefore, some strategies to avoid contact corrosion via the pretreatment and joining process are presented additionally.
Source: Materials and Corrosion
Authors: Jochen Schanz, Sara Nester, Dieter Meinhard, Timo Pott, Harald Riegel, Anjali K. M. De Silva, David K. Harrison, Volker Knoblauch
Institutions: Glasgow Caledonian University, Hochschule Aalen
Language: English
Subfield: Mechanics of Materials
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,700
Awards: FH-Impuls 2016: 'Innovative Fügeverfahren und beanspruchungsgerechte Designkonzepte für hybride Leichtbau CFK-Multimaterialverbunde (InDiMat)' im Gesamtvorhaben 'Smarte Materialien und intelligente Produktionstechnologien für energieeffiziente Produkte der Zukunft (SmartPro)', G7408118937, FH-Impuls 2016: Korrosionsprüfung für den Hybriden Leichtbau (KorLe)
OpenAlex ID: W3210000020