Impact of lanthanum doping on crystal structure and magnetic anisotropy of Mn-Zn soft nanoferrites

Year: 2025

Type: article

Abstract: The synthesis of lanthanum (La) substituted Zn (Mn 0.6 Zn 0.2 La 0.2 Fe 2 O 4 ) and Fe (Mn 0.6 Zn 0.4 La 0.2 Fe 1.8 O 4 ) was performed using sol-gel auto-combustion techniques to investigate the effects of lanthanum doping on the structural and magnetic properties of Mn-Zn nanoferrites. X-ray diffraction and transmission electron microscopy confirmed the development of a single-phase spinel structure and a reduction in crystallite size (from 16 to 10.7 nm) with La substitution. Although saturation magnetization (M s ) decreased due to changes in cation distribution and magnetic interactions, La doping led to an increase in initial permeability. This enhancement was linked to changes in M s and the magneto-crystalline anisotropy constant (K 1 ). The permeability loss factor (tan δ µ ) remained low (around 10 − 2 ) for the La-doped ferrites, indicating minimal energy loss at room temperature. These results suggest promising potential for advanced biomedical applications, in line with Sustainable Development Goals (SDGs). The sol-gel auto-combustion technique provides a scalable and environmentally friendly method for synthesizing these materials, supporting SDG targets related to responsible consumption and production (SDG 12).

Source: Scientific Reports

DOI: 10.1038/s41598-025-91305-4