Atomic layer etching of silicon nitride using infrared annealing for short desorption time of ammonium fluorosilicate
Year: 2017
Type: article
Abstract: An atomic layer etching process for silicon nitride (Si 3 N 4 ) has been developed in which ammonium fluorosilicate [(NH 4 ) 2 SiF 6 ] is formed and desorbed using infrared annealing. The cycle of forming and removing ammonium fluorosilicate was repeated, demonstrating that the Si 3 N 4 etching depth was accurately controlled with high selectivity to SiO 2 by changing the number of cycle. An X-ray photoelectron spectroscopy peak, which had been previously assigned as N–H bond of an ammonium salt, was observed after radical exposure, indicating that the ammonium fluorosilicate-based modified layer had formed. This peak disappeared after infrared annealing for 10 s, demonstrating desorption of the modified layer. In thermal desorption spectroscopy, NH 3 , HF, and SiF x were detected, providing further evidence for the formation of the ammonium fluorosilicate-based modified layer. In addition, this layer has a multilayer structure, protecting the Si 3 N 4 from exposure to reactive radicals.
Authors: Nobuya Miyoshi, Hiroyuki Kobayashi, Kazunori Shinoda, Masaru Kurihara, Tomoyuki Watanabe, Yutaka Kouzuma, Kenetsu Yokogawa, Satoshi Sakai, Masaru Izawa
Institutions: Hitachi (Japan), Hitachi High-Tech (Japan)
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $2,210
OpenAlex ID: W2609901458